TAARIFA YA MATOKEO
SAAFI YA ALUMINIUM A383 （ADC12 ）
A383 alloy ya aluminium, inayojulikana pia kama ADC12, ni aina ya alloy inayotumika kiasi kikubwa katika die casting inayotajika kwa nguvu kubwa, uvumbuzi mzuri, na upinzani wa uvimbo. Huu umbo hutumika mara kwa mara katika maombile ambayo yanahitaji miundo ya sehemu ngumu na uso wenye ubonye bwa giza.
Sifa za fisikali
|
Aluminium Alloy A383 |
Wiani |
Kupunguza UWIANO |
Joto Maalum |
Thermal Uongozi |
Kihifadhi Uongozi |
Thermal Upanuzi |
|
Kitengo cha Kiingereza |
lb/in³ |
℉ |
BTU/lb ℉ |
BTU/ft hr ℉ |
% IACS |
µ in/in ℉ |
|
Thamani |
0.099 |
960~108 |
0.230 |
55.6 |
23 |
11.7 |
|
Kitengo cha Mitro |
g/cm³ |
°C |
J/Kg °C |
W/mK |
% IACS |
µ m/m °K |
|
Thamani |
2.74 |
516~582 |
963 |
96.2 |
23 |
21.1 |
SIFATU ZA KIMETALI
|
WANDAZI WA ALUMINIUM A383 |
Ungano wa kuzingatia Nguvu |
KUPOTEA Nguvu |
Upanuzi n |
Ugumu |
KUVUNJA Nguvu |
Uchovu Nguvu |
|
Kitengo cha Kiingereza |
KSI |
KSI |
% katika 2in |
Brinell (HB) |
KSI |
KSI |
|
Thamani |
45 |
22 |
3.5 |
75 |
/ |
21 |
|
Mitindo ya Kimoa t |
MPa |
MPa |
% katika 51mm |
Brinell (HB) |
MPa |
MPa |
|
Thamani |
310 |
152 |
3.5 |
75 |
/ |
145 |
Ung'ano wa Kimia
|
Aluminium Ugatuzi wa die casting Vitunguu |
Maelezo |
|||||||||||
|
S i |
Fe |
Cu |
Mg |
Mn |
Ni |
Zn |
Sn |
Ti |
Nyingine Metali |
Al |
||
|
Wandazi wa Al A383(%) |
Asili |
9.5 |
0.0 |
2.0 |
0.00 |
0.00 |
0.00 |
0.0 |
0.00 |
0.00 |
0.0 |
Sambamba |
|
Max |
11.5 |
1.3 |
3.0 |
0.10 |
0.50 |
0.30 |
3.0 |
0.15 |
0.00 |
0.50 |
||
TAARIFA YA MATOKEO
SANDUKU LA ALUMINIUM A380 （ADC10 ）
Sanduku la aluminium A380 ni sanamu ya kawaida ya kupeperusha kwa uwezo wake mzuri wa kupitishwa na uwezo wa kujaza, unaoleta uzuri wa kutengeneza sehemu ngumu za kupeperusha. Kipengele chake kizuri cha nguvu, uvumbuzi, upinzani wa korosi, na upinzani wa kuchemka kimeifanya iwe sawa kwa matumizi mengi.
Sifa za fisikali
|
Aluminium Sanduku A38 0 |
Wiani |
Kupunguza UWIANO |
Joto Maalum |
Thermal Uongozi |
Kihifadhi Uongozi |
Thermal Upanuzi |
|
Kitengo cha Kiingereza |
lb/in³ |
℉ |
BTU/lb ℉ |
BTU/ft hr ℉ |
% IACS |
µ in/in ℉ |
|
Thamani |
0.099 |
1000~1100 |
0.230 |
55.6 |
23 |
12.1 |
|
Kitengo cha Mitro |
g/cm³ |
°C |
J/Kg °C |
W/mK |
% IACS |
µ m/m °K |
|
Thamani |
2.71 |
540~595 |
963 |
96.2 |
23 |
21.8 |
SIFATU ZA KIMETALI
|
Sanduku la Aluminium A38 0 |
Ungano wa kuzingatia Nguvu |
KUPOTEA Nguvu |
Upanuzi n |
Ugumu |
KUVUNJA Nguvu |
Uchovu Nguvu |
|
Kitengo cha Kiingereza |
KSI |
KSI |
% katika 2in |
Brinell (HB) |
KSI |
KSI |
|
Thamani |
47 |
23 |
3.5 |
80 |
27 |
20 |
|
Mitindo ya Kimoa t |
MPa |
MPa |
% katika 51mm |
Brinell (HB) |
MPa |
MPa |
|
Thamani |
324 |
159 |
3.5 |
80 |
186 |
138 |
Ung'ano wa Kimia
|
Aluminium Ugatuzi wa die casting Vitunguu |
Maelezo |
|||||||||||
|
S i |
Fe |
Cu |
Mg |
Mn |
Ni |
Zn |
Sn |
Ti |
Nyingine Metali |
Al |
||
|
Sanduku la Al A38 0(%) |
Asili |
7.5 |
0.0 |
3.0 |
0.00 |
0.00 |
0.00 |
0.0 |
0.00 |
0.00 |
0.00 |
Sambamba |
|
Max |
9.5 |
1.3 |
4.0 |
0.30 |
0.50 |
0.50 |
3.0 |
0.35 |
0.00 |
0.50 |
||
TAARIFA YA MATOKEO
SAAFI YA ALUMINIUM A383 （ADC12 ）
A383 alloy ya aluminium, inayojulikana pia kama ADC12, ni aina ya alloy inayotumika kiasi kikubwa katika die casting inayotajika kwa nguvu kubwa, uvumbuzi mzuri, na upinzani wa uvimbo. Huu umbo hutumika mara kwa mara katika maombile ambayo yanahitaji miundo ya sehemu ngumu na uso wenye ubonye bwa giza.
Sifa za fisikali
| Aluminium Alloy A383 | Wiani | Kupunguza UWIANO | Joto Maalum | Thermal Uongozi | Kihifadhi Uongozi | Thermal Upanuzi |
| Kitengo cha Kiingereza | lb/in³ | ℉ | BTU/lb ℉ | BTU/ft hr ℉ | % IACS | µ in/in ℉ |
| Thamani | 0.099 | 960~108 | 0.230 | 55.6 | 23 | 11.7 |
| Kitengo cha Mitro | g/cm³ | °C | J/Kg °C | W/mK | % IACS | µ m/m °K |
| Thamani | 2.74 | 516~582 | 963 | 96.2 | 23 | 21.1 |
SIFATU ZA KIMETALI
| WANDAZI WA ALUMINIUM A383 | Ungano wa kuzingatia Nguvu | KUPOTEA Nguvu | Upanuzi n | Ugumu | KUVUNJA Nguvu | Uchovu Nguvu |
| Kitengo cha Kiingereza | KSI | KSI | % katika 2in | Brinell (HB) | KSI | KSI |
| Thamani | 45 | 22 | 3.5 | 75 | / | 21 |
| Mitindo ya Kimoa t | MPa | MPa | % katika 51mm | Brinell (HB) | MPa | MPa |
| Thamani | 310 | 152 | 3.5 | 75 | / | 145 |
Ung'ano wa Kimia
| Aluminium Ugatuzi wa die casting Vitunguu | Maelezo | |||||||||||
| S i | Fe | Cu | Mg | Mn | Ni | Zn | Sn | Ti | Nyingine Metali | Al | ||
| Wandazi wa Al A383(%) | Asili | 9.5 | 0.0 | 2.0 | 0.00 | 0.00 | 0.00 | 0.0 | 0.00 | 0.00 | 0.0 | Sambamba |
| Max | 11.5 | 1.3 | 3.0 | 0.10 | 0.50 | 0.30 | 3.0 | 0.15 | 0.00 | 0.50 | ||
TAARIFA YA MATOKEO
SANDUKU LA ALUMINIUM A380 （ADC10 ）
Sanduku la aluminium A380 ni sanamu ya kawaida ya kupeperusha kwa uwezo wake mzuri wa kupitishwa na uwezo wa kujaza, unaoleta uzuri wa kutengeneza sehemu ngumu za kupeperusha. Kipengele chake kizuri cha nguvu, uvumbuzi, upinzani wa korosi, na upinzani wa kuchemka kimeifanya iwe sawa kwa matumizi mengi.
Sifa za fisikali
| Aluminium Sanduku A38 0 | Wiani | Kupunguza UWIANO | Joto Maalum | Thermal Uongozi | Kihifadhi Uongozi | Thermal Upanuzi |
| Kitengo cha Kiingereza | lb/in³ | ℉ | BTU/lb ℉ | BTU/ft hr ℉ | % IACS | µ in/in ℉ |
| Thamani | 0.099 | 1000~1100 | 0.230 | 55.6 | 23 | 12.1 |
| Kitengo cha Mitro | g/cm³ | °C | J/Kg °C | W/mK | % IACS | µ m/m °K |
| Thamani | 2.71 | 540~595 | 963 | 96.2 | 23 | 21.8 |
SIFATU ZA KIMETALI
| Sanduku la Aluminium A38 0 | Ungano wa kuzingatia Nguvu | KUPOTEA Nguvu | Upanuzi n | Ugumu | KUVUNJA Nguvu | Uchovu Nguvu |
| Kitengo cha Kiingereza | KSI | KSI | % katika 2in | Brinell (HB) | KSI | KSI |
| Thamani | 47 | 23 | 3.5 | 80 | 27 | 20 |
| Mitindo ya Kimoa t | MPa | MPa | % katika 51mm | Brinell (HB) | MPa | MPa |
| Thamani | 324 | 159 | 3.5 | 80 | 186 | 138 |
Ung'ano wa Kimia
| Aluminium Ugatuzi wa die casting Vitunguu | Maelezo | |||||||||||
| S i | Fe | Cu | Mg | Mn | Ni | Zn | Sn | Ti | Nyingine Metali | Al | ||
| Sanduku la Al A38 0(%) | Asili | 7.5 | 0.0 | 3.0 | 0.00 | 0.00 | 0.00 | 0.0 | 0.00 | 0.00 | 0.00 | Sambamba |
| Max | 9.5 | 1.3 | 4.0 | 0.30 | 0.50 | 0.50 | 3.0 | 0.35 | 0.00 | 0.50 | ||
TAARIFA YA MATOKEO
SANDUKU LA ALUMINIUM A360
Kiwango cha A360 cha silumin ni chaguo kizuri katika uvunduzi kwa sababu ya yasiyo ya juu ya silikoni, ambayo inaboresha uwezo wa kuimbana na ujazo, ukiruhusu uzalishaji wa vipande vya uvunduzi vinavyohitaji muundo mzito. Kina sifa bora za kiwango, upinzani wa uvamizi, na upinzani wa joto, ambalo hufanya kuwa chaguo bora kwa matumizi mengi.
Sifa za fisikali
| Aluminium Silumin A360 | Wiani | Kupunguza UWIANO | Joto Maalum | Thermal Uongozi | Kihifadhi Uongozi | Thermal Upanuzi |
| Kitengo cha Kiingereza | lb/in³ | ℉ | BTU/lb ℉ | BTU/ft hr ℉ | % IACS | µ in/in ℉ |
| Thamani | 0.095 | 1035~1105 | 0.230 | 65.3 | 29 | 11.6 |
| Kitengo cha Mitro | g/cm³ | °C | J/Kg °C | W/mK | % IACS | µ m/m °K |
| Thamani | 2.63 | 557~596 | 963 | 113 | 29 | 21.0 |
SIFATU ZA KIMETALI
| Silumin A360 | Ungano wa kuzingatia Nguvu | KUPOTEA Nguvu | Ukong'era | Ugumu | KUVUNJA Nguvu | Uchovu Nguvu |
| Kitengo cha Kiingereza | KSI | KSI | % katika 2in | Brinell (HB) | KSI | KSI |
| Thamani | 46 | 24 | 3.5 | 75 | 26 | 18 |
| Kitengo cha Mitro | MPa | MPa | % katika 51mm | Brinell (HB) | MPa | MPa |
| Thamani | 317 | 165 | 3.5 | 75 | 179 | 124 |
Ung'ano wa Kimia
| Aluminium Ugatuzi wa die casting Vitunguu | Maelezo | |||||||||||
| Si | Fe | Cu | Mg | Mn | Ni | Zn | Sn | Ti | Nyingine Metali | Al | ||
| Silumin A360(%) | Asili | 9.0 | 0.0 | 0.0 | 0.4 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | Sambamba |
| Max | 10.0 | 1.3 | 0.6 | 0.6 | 0.35 | 0.50 | 0.50 | 0.15 | 0.00 | 0.25 | ||
TAARIFA YA MATOKEO
SILUMIN B390
Silumin A413 inajulikana kwa uwezo wake mkubwa wa kuzuia shinikizo, ambao unafanya kuwa ni nyenzo nzuri kwa silinda za hydraulic. Sifa zake bora za uvunduzi zinamfanya kuwa chaguo bora kwa uvunduzi wa vipengele vinavyotegemea ufasaha.
Sifa za fisikali
| Aluminium Silumin A 413 | Wiani | Kupunguza UWIANO | Joto Maalum | Thermal Uongozi | Kihifadhi Uongozi | Thermal Upanuzi |
| Kitengo cha Kiingereza | lb/in³ | ℉ | BTU/lb ℉ | BTU/ft hr ℉ | % IACS | µ in/in ℉ |
| Thamani | 0.096 | 1065~1080 | 0.230 | 70.1 | 31 | 11.9 |
| Kitengo cha Mitro | g/cm³ | °C | J/Kg °C | W/mK | % IACS | µ m/m °K |
| Thamani | 2.66 | 574~582 | 963 | 121 | 31 | 21.6 |
SIFATU ZA KIMETALI
| Silumin A 413 | Ungano wa kuzingatia Nguvu | KUPOTEA Nguvu | Upanuzi n | Ugumu | KUVUNJA Nguvu | Uchovu Nguvu |
| Kitengo cha Kiingereza | KSI | KSI | % katika 2in | Brinell (HB) | KSI | KSI |
| Thamani | 42 | 19 | 3.5 | 80 | 25 | 19 |
| Mitindo ya Kimoa t | MPa | MPa | % katika 51mm | Brinell (HB) | MPa | MPa |
| Thamani | 290 | 131 | 3.5 | 80 | 172 | 131 |
Ung'ano wa Kimia
| Aluminium Ugatuzi wa die casting Vitunguu | Maelezo | |||||||||||
| S i | Fe | Cu | Mg | Mn | Ni | Zn | Sn | Ti | Nyingine Metali | Al | ||
| Silumin A 413(%) | Asili | 11.0 | 0.0 | 0.0 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | Sambamba |
| Max | 13.0 | 1.3 | 1.0 | 0.10 | 0.35 | 0.50 | 0.50 | 0.15 | 0.00 | 0.25 | ||
TAARIFA YA MATOKEO
SILUMIN B390
B390 ya alimini ni yenye upepo mkubwa wa kuvamia kutokana na yake ya juu ya silikoni na magnesiamu. Pia ina sifa bora za kiashiria na upinzani wa uvamizi, ikitumika kwa matumizi mengi.
Sifa za fisikali
| Aluminium Alloy B390 | Wiani | Kupunguza UWIANO | Joto Maalum | Thermal Uongozi | Kihifadhi Uongozi | Thermal Upanuzi |
| Kitengo cha Kiingereza | lb/in³ | ℉ | BTU/lb ℉ | BTU/ft hr ℉ | % IACS | µ in/in ℉ |
| Thamani | 0.098 | 950~1200 | / | 77.4 | 27 | 10.0 |
| Kitengo cha Mitro | g/cm³ | °C | J/Kg °C | W/mK | % IACS | µ m/m °K |
| Thamani | 2.71 | 510~650 | / | 134 | 27 | 18.0 |
SIFATU ZA KIMETALI
| Aluminum Alloy B390 | Ungano wa kuzingatia Nguvu | KUPOTEA Nguvu | Ukong'era | Ugumu | KUVUNJA Nguvu | Uchovu Nguvu |
| Kitengo cha Kiingereza | KSI | KSI | % katika 2in | Brinell (HB) | KSI | KSI |
| Thamani | 46 | 36 | chini ya 1 | 120 | / | 20 |
| Kitengo cha Mitro | MPa | MPa | % katika 51mm | Brinell (HB) | MPa | MPa |
| Thamani | 317 | 248 | chini ya 1 | 120 | / | 138 |
Ung'ano wa Kimia
| Aluminium Ugatuzi wa die casting Vitunguu | Maelezo | |||||||||||
| Si | Fe | Cu | Mg | Mn | Ni | Zn | Sn | Ti | Nyingine Metali | Al | ||
| Al Alloy B390(%) | Asili | 16.0 | 0.0 | 4.0 | 0.45 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | Sambamba |
| Max | 18.0 | 1.3 | 5.0 | 0.65 | 0.50 | 0.10 | 1.50 | 0.00 | 0.20 | 0.20 | ||
EN